- Considerations on indirect adhesive restorations at the material and tooth interfaces
- Del Bianco, Federico <1989>
Subject
- MED/28 Malattie odontostomatologiche
Description
- Objective: Lithium-silicate (LiSi) ceramic is nowadays widely used in dentistry. However, for the longevity of LiSi indirect restorations, it is important to pretreat the material and the dental substrate adequately. However, is not certain how the simplification of the manufacturing and conditioning procedures influences the bonding performances of LiSi ceramic restorations. Accordingly, the aims of this thesis were to investigate the effect of: 1) different LiSi ceramic surface decontamination procedures on the shear bond strength (SBS) to resin composite; 2) different types of lithium-disilicate (LiDi) (pressed vs CAD-CAM) on SBS to resin composite; 3) an experimental metal salt-based zirconium oxynitrate etchant [ZrO(NO3)2] on bonding performances to dentin. Materials and Methods: SBS test was used to investigate the influence of different cleaning protocols applied, or different processing techniques (CAD or PRESS) on the bond strength to composite resin. The third study tackled the interface between restorative materials and dentin, and investigated the microtensile bond strength test (µTBS), nanoleakage expression analysis (NL), gelatin zymography and in situ zymography of dentin conditioned with an experimental metal salt-based zirconium oxynitrate etchant [ZrO(NO3)2]. Results: MEP showed comparable bond strength to the double HP etching and higher compared to other groups. BS of press LiSi to composite was higher than that of CAD/CAM LiSi. ZON pretreatment increased bond strength to dentin when used with a universal adhesive, and inhibited dentinal endogenous enzymes. Conclusions: While simplification of the LiSi conditioning and cleaning procedures seems to yield bond strength comparable to the traditional procedures, it could be recommended in the clinical practice. However, pressed LiSi still seems to perform better in terms of bond strength compared to the CAD/CAM LiSi. Further, the novel ZON etchant seems to perform better compared to the traditional phosphoric dentin etching.
Date
- 2023-03-30
- info:eu-repo/date/embargoEnd/2024-06-02
Type
- Doctoral Thesis
- PeerReviewed
Format
- application/pdf
Identifier
urn:nbn:it:unibo-29830
Del Bianco, Federico (2023) Considerations on indirect adhesive restorations at the material and tooth interfaces, [Dissertation thesis], Alma Mater Studiorum Università di Bologna. Dottorato di ricerca in Scienze biomediche e neuromotorie